微波连续合成纳米TiC粉体影响因素分析
Analysis of the Influencing Factors in the Microwave and Continuum Preparation of Nano TiC Powders

作者: 周其星 , 曾令可 * , 刘平安 , 刘 阳 , 王 慧 :华南理工大学; 刘艳春 :广州红日燃具有限公司;

关键词: 微波合成纳米TiC合成率粒度Microwave Synthesis Nanometer TiC Synthesis Rate Particle Size

摘要:

本文利用微波连续合成纳米TiC粉体,并运用透射电镜(TEM)、激光粒度分析及X射线衍射分析(XRD)等分析手段测定了纳米TiC粉体的成分和粒度分布及大小。探讨了原料粒度、合成温度、合成时间、保温时间等关键影响因素与产品合成率、粒度大小分布的相互关系。实验结果表明,合成TiC最佳条件如下:原料(TiO2)粒度为30 nm,合成温度为1300℃~1400℃,合成时间为60 min,保温时间(1300℃)为30 min。

Abstract: In this article the nanometer TiC powder was synthesized by the method of continuous microwave, and its composition and particle size distribution were determined by using TEM, Acoustic particle size analysis (APS) and XRD. The effect of raw materials particle size, synthesis temperature and holding time on the nanometer TiC synthesis was discussed. The experimental results show that the best synthetic conditions are as follows: raw materials (TiO2) size is 30 nm, synthesis temperature is between 1300˚C and 1400˚C, synthetic time for 60 min, the best heat preservation time (1300˚C) is 30 min.

文章引用: 周其星 , 曾令可 , 刘平安 , 刘 阳 , 刘艳春 , 王 慧 (2012) 微波连续合成纳米TiC粉体影响因素分析。 纳米技术, 2, 44-49. doi: 10.12677/NAT.2012.23009

参考文献

[1] 刘阳, 曾令可, 胡晓力等. 碳化钛的合成及其应用研究进展[J]. 中国陶瓷, 2002, 38(5): 7-10.

[2] 陈怡元, 邹正光, 龙飞. 碳化钛基金属陶瓷的合成及其应用研究现状[J]. 钛工业进展, 2007, 24(3): 5-9.

[3] 王为民, 傅正义, 袁润章. TiC纳米晶粉的制备及其特性[J]. 陶瓷学报, 1998, 19(2): 73-75.

[4] 李奎, 潘复生, 汤爱涛. TiC、TiN、Ti(C、N)粉末制备技术的现状及发展[J]. 重庆大学学报(自然科学版), 2002, 25(6): 135- 138.

[5] K. Rasit. Kinetics and phase evolution during carbothermal syn- thesis of titanium carbide ultrafine titnina/carbon mixture. Jour- nal of Materials Science, 1998, 33(4): 1049-1055.

[6] J. F. Li, Z. Q. Zhang. Self-propagating high-temperature synthesis of (W,Ti)C powder. Journal of Central South University of Techolgy, 1999, 6(2): 124-126.

[7] R. Alexandrescu. Synthesis of TiC and SiC/TiC nanocrystalline powders by gaw-phase laser-induced reaction. Journal of Mate- rials Science, 1997, 32(2): 5629-5635.

[8] G. Cliche. Synthesie of TiC and (Ti,W)C in solvent metals. Ma- terials Science and Engineering A, 1991, 148(2): 319-328.

[9] M. S. Hsu. Synthesis of nanocrystalline titanium carbide by spark erosion. Scripta Metallurgica et Materialia, 1995, 32(6): 805-808.

[10] C. Chul-Jin. Perparation of ultrafine TiC-Ni cermet powders by mechanical alloying. Journal of Materials Processing Technoligy, 2000, 104(1): 127-132.

[11] 李劲风, 张昭, 张鉴清等. W含量及预热温度对Ti-W-C体系燃烧合成产物的影响研究[J]. 稀有金属材料科学与工程, 2002, 31(1): 64-68.

分享
Top