航空用高导电硅橡胶设计及性能研究
Design and Performance Study of High Conductive Silicone Rubber for Aviation

作者: 张 锐 * , 王 喆 :中国电子科技集团公司第三十三研究所,山西 太原;

关键词: 高导电硅橡胶玻璃镀银微珠铝镀银电性能力学性能环境适应性High Conductive Silicone Rubber Silver Coated Glass Beads Silver Plated Aluminum Electrical Properties Mechanical Properties Environmental Adaptability

摘要:
本文通过高导电硅橡胶配方中硅橡胶和导电填料的选型和测试的实验,对硫化合成后的玻璃镀银微珠导电橡胶和铝镀银导电橡胶进行一系列环境试验前后指标的对比研究,研究结果表明采用30度级且平均分子量120万的乙烯基硅橡胶和平均粒径40 µm的铝镀银或玻璃镀银填料制成的高导电硅橡胶具有优秀的电性能、力学性能和环境适应性能。

Abstract: In this paper, through the selection and testing of silicone rubber and conductive filler in high conductive silicone rubber formulation, a comparative study of indexes before and after a series of environmental tests was conducted on the glass coated silver coated micro conductive rubber and aluminum silver plated conductive rubber. The results show that high conductive silicone rubber, made of the vinyl silicone rubber of 30 degree and the average molecular weight of 1 million 200 thousand and the aluminum silver or silver plated glass filler of the average particle size of 40 µm, has excellent electrical properties, mechanical properties and environment properties.

文章引用: 张 锐 , 王 喆 (2017) 航空用高导电硅橡胶设计及性能研究。 材料化学前沿, 5, 31-36. doi: 10.12677/AMC.2017.52004

参考文献

[1] 陈元章. 军用电子设备的防护技术[J]. 航天工艺, 1997(5): 35-37.

[2] 郭颜萍. 电磁屏蔽技术在电子设备中的应用[J]. 山东科学, 2005, 18(5): 48-51.

[3] 生楚君. 高电导率导电橡胶的研制及应用[J]. 电子工艺技术, 1997, 18(5): 191.

[4] 武学高. 塑料电镀技术[M]. 成都: 四川科技出版社, 1994: 366-372.

[5] Dlouhy, I. and Boccaccini, R. (1996) Preparation Microstructure and Mechanical Properties of Metal Particulate/Glass Matrix Composite. Composites Science and Technology, 6, 1415-1424.

[6] 蔡楚江, 俞晓正, 沈志刚, 等. 空心微珠表面金属化研究[J]. 现代化工, 2006, 26(s1): 241-244.

[7] 张辉, 孙洁, 沈兰萍. 空心微珠化学镀银研究[J]. 电镀与涂饰, 2007, 26(1): 26-29.

[8] 王宇, 张骁勇, 毛丽. 空心玻璃微珠化学镀银的研究[J]. 材料科学与工程学报, 2004, 22(5): 753-756.

分享
Top