冷却速率对轴承钢GCr15组织和性能的影响
Effect of Cooling Rate on Microstructures and Properties of GCr15 Bearing Steel

作者: 王银国 , 董凤奎 , 何健楠 :宝钢特钢韶关有限公司,广东 韶关; 孙福猛 , 李祥龙 , 李世晶 :宝钢集团广东韶关钢铁有限公司,广东 韶关;

关键词: 轴承钢GCr15CCT曲线冷却工艺网状碳化物Bear Steel GCr15 CCT Curve Cooling Process Net Carbide

摘要:
本文采用光学显微镜、显微硬度等分析手段对某钢厂生产的GCr15轴承钢在不同冷却速度下的奥氏体相变规律进行了研究。结果表明:发生珠光体相变的临界冷却速度约为3℃/s,当温度降至约200℃时,发生马氏体转变。冷却速度小于5℃/s时,会产生较严重的网状碳化物,随冷却速度的提高,网状碳化物析出减少,珠光体相变温度降低。

Abstract: The Austenite phase transformation law of GCr15 bearing steel with different processes is studied by means of optical microscope and hardness tester. The experimental results show that: the critical cooling rate of pearlite phase transformation is about 3˚C/s and the Martensite transfor-mation starts when the temperature drops at about 200˚C. There will be a serious precipitation of net carbide when the cooling rate is less than 5˚C/s, and with the increase of cooling rate, the pearlite phase transformation temperature becomes lower and the precipitation of net carbide decreases.

文章引用: 王银国 , 孙福猛 , 董凤奎 , 何健楠 , 李祥龙 , 李世晶 (2016) 冷却速率对轴承钢GCr15组织和性能的影响。 冶金工程, 3, 99-105. doi: 10.12677/MEng.2016.32015