重晶石粉末表面偶联剂改性和表征
Surface Modification of Barite Powder by Coupling Agent and Characterization

作者: 雷廷廷 , 徐 妍 , 王李婷 , 单树楠 :上海师范大学生命与环境科学学院化学系,上海; 邓 磊 , 朱丽锦 :上海腾民实业有限公司,上海;

关键词: 重晶石偶联剂表面改性Barite Coupling Agent Surface Modification

摘要:
利用自制的钛酸酯偶联剂,采用干法改性工艺,对天然重晶石表面进行改性研究,测试了改性前后重晶石吸油量、接触角、活化指数等性能指标,通过对比发现改性后重晶石表面性能有了明显改变,达到了从亲水性向疏水性的转变。粒径分布结果表明改性后颗粒未发生明显团聚现象,而通过扫描电子显微镜、热重和傅里叶变换红外光谱分析表征,观察到颗粒形貌,失重率及表面状态的变化,验证了其改性后偶联剂与重晶石的表面键合作用,并由此为基础探讨了其改性机理。

Abstract: Natural barite powder was modified with the method of surface coating by self-made titanate coupling agent. The effect of modification was evaluated by the oil absorption value, contact angle, activation index, and particle size distribution. By comparison, there is significant change on the surface performance of barite after modification, from hydrophility to hydrophobicity. No obvious aggregation of particles was found by the result of particle size distribution. Through the characterization of FTIR, SEM, and thermal analysis, the change of morphology, weight loss ratio, and surface state were observed. These results verified the chemical bonding between the titanate coupling agent and the surface of barite after modification. Based on the results, the modification mechanism was discussed.

文章引用: 雷廷廷 , 徐 妍 , 王李婷 , 单树楠 , 邓 磊 , 朱丽锦 (2015) 重晶石粉末表面偶联剂改性和表征。 自然科学, 3, 113-120. doi: 10.12677/OJNS.2015.34015

参考文献

[1] 肖琴, 满瑞林, 杨萍, 尹晓莹, 常伟. 十二烷基硫酸钠改性重晶石的研究[J]. 非金属矿, 2013(36): 5-7.

[2] Ipek, H., Ucba, Y., Yekeler, M. and Hosten, C. (2005) Dry Grinding Kinetics of Binary Mixtures of Ceramic Raw Materials by Bond Milling. Ceramics International, 31, 1065-1071.
http://dx.doi.org/10.1016/j.ceramint.2004.11.006

[3] Abdul Khali, H.P.S. and Ismail, H. (2000) Effect of Acetylation and Coupling Agent Treatments upon Biological Degradation of Plant Fibre Reinforced Polyester Composites. Polymer Testing, 20, 65-75.
http://dx.doi.org/10.1016/S0142-9418(99)00080-X

[4] 钱逢麟, 竺玉书. 涂料助剂[M]. 北京: 化学工业出版社, 1990.

[5] Della Volpe, C., Penati, A., Peruzzi, R., Siboni, S., Toniolo, L. and Colombo, C. (2000) The Combined Effect of Roughness and Heterogeneity on Contact Angles: The Case of Polymer Coating for Stone Protection. Journal of Adhesion Science and Technology, 14, 273-299.
http://dx.doi.org/10.1163/156856100742555

[6] 王威, 欧阳兆辉. 重晶石矿粉表面改性研究与应用[J]. 中国非金属矿工业导刊, 2005(6): 37-39.

[7] 钱海燕, 叶旭初, 张少明. 非金属矿粉体改性及效果评价[J]. 非金属矿, 2001(21): 10-12.

[8] 梁晨. 天然重晶石粉末表面改性及工艺流程设计探讨[J]. 地球, 2013(3): 279.

[9] 余海峰, 张玲, 包华, 李春忠. 钛酸酯偶联剂改性纳米CaCO3/PVC的结构和性能[J]. 华东理工大学学报(自然科学版), 2005(1): 119-121.

[10] 胡春艳. 天然重晶石粉末表面改性及工艺流程设计[D]: [硕士论文]. 重庆: 重庆大学, 2010.

[11] 蒋建平, 陈小文, 贾欣茹. 单烷氧基钛酸酯偶联剂在涂料中的应用[J]. 中国涂料, 2006(6): 35-36.

[12] 杨少华, 崔英德, 孙福祥. 超细硫酸钡的制备及其表面改性[J]. 广州化工, 2002(30): 27-31.

分享
Top