SGP的力学性能研究综述
Review on Studies on Mechanical Properties of SGP

作者: 邵 筱 , 陈素文 :同济大学土木工程学院,上海;

关键词: SGP力学性能温度敏感试验研究应变率相关SGP Mechanical Property Temperature Sensitive Experimental Study Strain-Rate Dependence

摘要:
聚乙烯醇缩丁醛中间膜(PVB)在过去几十年被广泛应用于夹层玻璃中。如今新型的离子性中间膜(SGP)较之PVB具有更好的强度和刚度,SGP的采用使得夹层玻璃从之前的仅仅作为安全玻璃发展为结构的一部分。基于其良好的力学性能,SGP在幕墙结构中得到越来越广泛的应用,特别是一些超高层和大型城市公共建筑。然而,到目前为止,对SGP的力学性能尚未有系统的研究,这对夹层玻璃的设计造成了一定困难。本文主要介绍了国内外关于SGP力学性能的研究现状,并根据试验目的和方法的不同进行了归纳总结。

Abstract: Polyvinyl butyral (PVB) has been widely adopted for interlayer in laminated glass in the past dec-ades. Nowadays, a new interlayer SentryGlas®Plus (SGP) has been developed, which has better stiffness and strength compared with PVB. SGP’s application makes laminated glass not only to be shatterproof glass, but to be a part of the structure. Due to its superior mechanical properties, SGP gains more and more application in curtain wall structures, especially in super high-rise buildings and large-scale public buildings. Nevertheless, there is no systematic study on SGP’s mechanical property, which causes some difficulties in the design of laminated glass. This paper reviews the present researches on mechanical performance of the SGP around the world.

文章引用: 邵 筱 , 陈素文 (2015) SGP的力学性能研究综述。 土木工程, 4, 143-150. doi: 10.12677/HJCE.2015.43018

参考文献

[1] (2005) DuPont™SentryGlas®-brochure. The USA. www.dupont.com/safetyglass

[2] (2008) DuPont™SentryGlas® Post-breakage strength. The USA. www.dupont.com/safetyglass

[3] (2008) DuPont™SentryGlas®-visual quality. The USA. www.dupont.com/safetyglass

[4] DuPont™. http://www2.dupont.com/SafetyGlass/en_US/assets/pdfs/sgx_lightfastness.pdf (2004) SentryGlas® Expressions™-Lightfastness. www.dupont.com/safetyglass

[5] (2008) Du-Pont™SentryGlas®-UV control. The USA. www.dupont.com/safetyglass

[6] (2011) Du-Pont™SentryGlas®-weathering. The USA. www.dupont.com/safetyglass

[7] (2010) DuPont™SentryGlas®-edge stability. The USA. www.dupont.com/safetyglass

[8] (2011) Ceramic frit compatibility with SentryGlas®. The USA. www.dupont.com/safetyglass

[9] (2011) DuPont™SentryGlas®-sealant compatibility. The USA. www.dupont.com/safetyglass

[10] Delincé, D., Sonck, D., Belis, J., et al. (2008) Experimental investigation of the local bridging behaviour of the interlayer in broken laminated glass. ISAAG Conference Proceedings, Munchen, 19-21.

[11] Delincé, D., Callewaert, D., Belis, J. and Van Impe, R. (2008) Post-breakage behavior of laminated glass in structural applications. Proceedings of the Conference on Architectural and Structural Applications of Glass, Delft, 22-23 May 2008, 459-467.

[12] Bennison, S.J., Qin, M.H.X. and Davies, P.S. (2008) High-performance laminated glass for structurally efficient glazing in innovative light-weight structures and sustainable facades. Hong Kong, May 2008, 1-12.

[13] Callewaert, D. and Delincé, D. (2009) Laminated glass as a structural building material. UGent-FirW Doctoraatssymposium, 10e, 160-161.

[14] 中国建材检验认证集团股份有限公司和国家安全玻璃及石英玻璃质量监督检验中心 (2013) 层玻璃中间层材料的剪切模量的测试的试验报告.

[15] Sobek, W., Kutterer, M. and Messmer, R. (1999) Shear stiffness of the interlayer in laminated glass. Proceedings of the 6th International Conference on Architectural and Automotive Glass (Glass Processing Days), Tampere, 13-16 June 1999, 360-365.

[16] 戎文杰 (2010) PVB材性及其对玻璃幕墙抗爆性能的影响研究. 硕士论文, 同济大学, 上海.

[17] Belis, J., Depauw, J., Callewaert, D., Delincé, D. and Van Impe, R. (2009) Failure mechanisms and residual capacity of annealed glass/SGP laminated beams at room temperature. Engineering Failure Analysis, 16, 1866-1875.

[18] Bennison, S.J., Smith, C.A., Van Duser, A., et al. (2001) Structural performance of laminated safety glass made with “Stiff” interlayers. Proceedings of the Seventh International Conference on Architectural and Automotive Glass (Glass Processing Days), Tampere, 18-21 June 2001, 18-21.

[19] Norville, H.S. and Conrath, E.J. (2001) Considerations for blast resistant glazing design. Journal of Architectural Engineering, 7, 80-86.

[20] Bennison, S., Sloan, J., Kistunas, D., Buehler, P., Amos, T. and Smith, C. (2005) Laminated glass for blast mitigation: Role of interlayer properties. Proceedings of the 9th International Conference on Architectural and Automotive Glass (Glass Processing Days), Tampere, 17-20 June 2005, 17-20.

[21] Bennison, S.J., et al. (2003) Expanding bomb blast performance of architectural glass. Proceedings of the 8th International Conference on Architectural and Automotive Glass (Glass Processing Days), Tampere, 15-18 June 2003, 15-18.

[22] Callewaert, D., et al. (2008) Temperature-dependent behavior of glass/ionomer laminates: Preliminary test results. Proceedings of Challenging Glass—Conference on Architectural and Structural Applications of Glass, Delft, 22-23 May 2008, 22-23.

[23] Scarpino, P., Kasper, R. and Sedlacek, G. (2004) Saint venantsche torsionswiderstände von querschnitten in sandwichbauweise. Bauingenieur, Band 79/2004, 167-175.

[24] Callewaert, D., Depaepe, J., De Vogel, K., Belis, J., Delincé, D. and Van Impe, R. (2008) Influence of Temperature and Load Duration on Glass/Ionomer Laminates: Torsion and Bending Stiffness. Conference Proceedings of ISAAG2008, Munich, 51-63.

[25] 赵西安 (2011) SGP夹层玻璃提高建筑幕墙安全性. 建设科技, 23, 60-63.

[26] 赵西安 (2012) 离子性中间膜夹层玻璃. 2012年全国铝门窗幕墙行业年会论文.

[27] 刘刚, 赵西安 (2009) 夹层玻璃高温受弯性能试验研究报告. 中国建筑科学研究院建筑结构研究所, 北京.

分享
Top