聚乙烯塑料–煤粉与铁精矿混合球团性能研究
Research on the Performance of Iron Ore Pellets Containing Coal and Polyethylene

作者: 刘 静 , 郭 锐 :安徽工业大学,安徽 马鞍山; 刘良轩 :安徽省东部矿山设计院,安徽 合肥; 刘 成 :马钢集团四钢轧总厂,安徽 马鞍山; 李文文 :马鞍山市工业经济联合会,安徽 马鞍山;

关键词: 聚乙烯塑料混合含碳球团直接还原还原度孔隙率Polyethylene Plastic Mixed Pellets Containing Carbon Direct Reduction Reducibility Porosity

摘要:
采用煤粉混合聚乙烯废塑料与铁精矿制备含碳球团,对所得混合含碳球团特性进行了试验研究。结果表明,在一定的物料粒度、水分含量、膨润土加入量条件下,配加聚乙烯塑料的混合含碳球团的冷态性能增强,塑料加入量越多,球团冷态强度越好,以干球强度提高更为明显。焙烧还原后,1:1的聚乙烯煤粉混合还原剂球团(或1:2)比煤粉球团强度增强,且对还原后的球团进行矿相分析发现,配加聚乙烯塑料能够改善自还原过程的热质条件,促进还原反应的进行,且还原区域集中在聚乙烯塑料颗粒周围。

Abstract: Experimental researches on characteristics of the mixed pellets containing carbon which are made from pulverized coal mixed with polyethylene plastic and iron ore were carried out. The results show that under certain material particle size, moisture content percent and certain amount of bentonite conditions, cold state performance of pellets containing carbon mixed with addition of polyethylene plastic is reinforced, meaning that the more amount of plastic added in the mixed pellets, the better the cold strength to increase the strength of the dry bulb apparently. After the roasting reduction, strength of pulverized reductant polyethylene pellets with mixed rates of 1:1 (or 1:2) is better than that of pulverized coal pellet, and mineralogical analysis on polyethylene pellets shows that the addition of polyethylene plastic can improve the conditions of the reducing process heat and promote the reducing reaction, and the reducing area concentrates around the polyethylene plastic particles.

文章引用: 刘 静 , 刘良轩 , 刘 成 , 李文文 , 郭 锐 (2015) 聚乙烯塑料–煤粉与铁精矿混合球团性能研究。 冶金工程, 2, 49-56. doi: 10.12677/MEng.2015.22008

参考文献

[1] 郭建龙, 赵俊学, 仇圣桃, 等 (2014) 废塑料在钢铁行业的应用现状及建议. 钢铁研究报报, 6, 1-4.

[2] 戴云阁, 李文秀, 等 (1998) 现代转炉炼钢. 东北大学出版社, 沈阳.

[3] 毕学工 (2008) 武钢炼铁CO2排放现状及减排方向. 炼铁, 1, 17-21.

[4] 任志国, 周渝生, 王来久, 等 (1996) 含碳冷固结球团矿冶金性能研究. 烧结球团, 6, 16-22.

[5] 杜挺, 杜昆 (1997) 含碳球团–铁浴熔融还原法关键技术的应用基础研究. 金属学报, 7, 718-727.

[6] 梁中渝 (2009) 炼铁学. 冶金工业出版社, 北京, 129-134.

[7] Zhang, Y.B., Li, G.H. and Jiang, T. (2011) Tin and Zinc separation from Tin, Zinc bearing complex iron ores by selective reduction process. Ironmaking Steelmaking, 46l, 613-619.

[8] 李建 (2007) 铁精矿复合粘结剂球团直接还原法工艺及机理研究. 硕士论文, 中南大学, 长沙, 123-127.

[9] 陈伟鹏, 谢智辉, 张欢, 等 (2014) 加入聚乙烯的含碳铁矿球团的直接还原. 过程工程学报, 5, 823-828.

[10] Murakami, T. and Kasai, E. (2011) Reduction mechanism of iron oxide-carbon composite with polyethylene at lower temperature. ISIJ International, 51, 9-13.