微波处理高砷铁矿石脱砷的试验研究
Experimental Study of Microwave Treating High Arsenic Ore

作者: 王刘涛 , 王海川 , 徐 飞 :安徽工业大学冶金工程学院,安徽 马鞍山 ; 陈鹏飞 :江苏永钢集团有限公司技术处,江苏 张家港;

关键词: 微波高砷铁矿石脱砷配碳量Microwave High Arsenic Ore Dearsenization Carbon Content

摘要:
利用微波加热的方法处理高砷铁矿石,在不同的配碳量下加热到850℃,950℃,1050℃,1150℃,保温10分钟,微波功率1 KW。试验结果表明:微波焙烧的脱砷效率比常规加热焙烧脱砷效率高,在配碳量为0%、4%、8%,马弗炉焙烧脱砷率为39.29%、69.51%、92.02%,而微波焙烧脱砷率为50.45%、88.66%、95.93%;脱砷率随着配碳量和焙烧温度的增加而增大,在配碳量为0%、4%、8%,平均脱砷率为44.87%、79.09%、92.97%,在850℃,950℃,1050℃,1150℃,平均脱砷率为63.75%、68.98%、77.97%、78.01%。

Abstract: The iron ore with high arsenic is heated to 850˚C, 950˚C, 1050˚C, 1150˚C in the different carbon content and kept thermal insulation for 10 min by microwave (1 kW) heating method. The result indicates that the dearsenification rate of microwave roasting is higher than the regular heating ways. The dearsenification roasting in Muffle furnace is 39.29%, 69.51%, 92.02% and that of mi-crowave roasting is 50.45%, 88.66%, 95.93% at respective carbon content of 0%, 4%, 8%. The dearsenification rises with the increase of the carbon content and the roasting temperature. The average dearsenification is 44.87%, 79.09%, 92.97% at respective carbon content of 0%, 4%, 8%; and at different temperature of 850˚C, 950˚C, 1050˚C, 1150˚C. The average dearsenification is 63.75%, 68.98%, 77.97%, 78.01%.

文章引用: 王刘涛 , 王海川 , 徐 飞 , 陈鹏飞 (2015) 微波处理高砷铁矿石脱砷的试验研究。 冶金工程, 2, 29-35. doi: 10.12677/MEng.2015.21005

参考文献

[1] 烧结厂、炼铁厂、钢铁研究所调查组 (1976) 使用含铅、锌、砷、锡、铜矿石的调查报告. 武钢技术, 2, 2-15.

[2] 吕庆, 张淑会 (2010) 含砷铁矿石烧结脱砷的试验研究. 钢铁, 6, 7-11.

[3] 张淑会, 吕庆 (2011) 含砷铁矿石脱砷过程热力学. 中国有色金属学报, 7, 1705-1712.

[4] 杨大锦, 左以专, 彭建蓉, 等 (2001) 高砷红土矿焙烧脱砷试验研究. 有色金属(炼铁部分), 3, 5-7.

[5] 梁英生 (1979) 炼钢过程中砷氧化的可能性——热力学计算与实践. 钢铁, 6, 35-42.

[6] 龚•H, 崔洪山, 太白 (2002) 硫砷铜矿在戊基钾黄药溶液中的电位和润湿性. 国外金属矿选矿, 12, 22-34.

分享
Top