发动机汽缸头螺栓断裂的正交试验研究
Orthogonal Experiment Research of Engine Cylinder Head Bolt Fracture

作者: 王正进 :新大洲本田摩托有限公司,上海;

关键词: 缸头螺栓螺纹折叠疲劳断裂Cylinder Head Screw Thread Folding Fatigue Fracture

摘要:

对摩托车发动机缸头螺栓断裂件进行了CTi失效失析分析。螺栓断裂处材质、硬度、抗拉强度、夹杂物均合格,基体显微组织回火索氏体正常,表面脱碳深度(8.3 um)也符合要求。但螺牙底部有折叠裂纹,不符合GB5779.3对螺牙缺陷的要求。推定以折叠裂纹为起源,而后在使用时裂纹扩展造成断裂。通过正交试验改进了螺纹滚压工艺六参数,消除了螺纹折叠。

Abstract: A CTi failure loss analysis is made on the motorcycle engine cylinder head bolt fracture. The material, hardness, tensile strength, inclusions in bolt split are qualified; the tempered sorbite of matrix microstructure is normal; surface decarburization depth (8.3 um) also meets the requirements. But there is a crack folded at the bottom of the screw tooth of screw tooth defect, which is not in conformity with the GB5779.3 requirements. Presuming folded crack as the origin, fracture occurs resulting from crack propagation when it is being used. Through the orthogonal experiment, the six parameters of thread rolling technology are improved and the thread folding is eliminated.

文章引用: 王正进 (2014) 发动机汽缸头螺栓断裂的正交试验研究。 机械工程与技术, 3, 49-56. doi: 10.12677/MET.2014.32007

参考文献

[1] 童孟曦 (2006) 汽车上的螺纹连接. 无锡南洋学院学报, 2, 50-53.

[2] 梅艳波 (2009) 螺纹加工方法研究. 长江大学学报(自然科学版), 1, 279-280.

[3] 方伟 (2000) 滚压活塞杆螺纹用滚丝轮制造技术. 压缩机技术, 162, 5-8.

[4] 刘风雷 (2005) 滚压加工技术提高高强度航空紧固件的疲劳强度. 航空制造技术, 6, 97-99.

[5] 崔长华 (1978) 螺纹的滚压加工. 机械工业出版社, 北京.

[6] 于献忠, 主编 (2008) 质量专业理论与实务. 中国人事出版社, 北京.

[7] 中华人民共和国国家标准 (2004) 紧固件表面缺陷螺栓、螺钉和螺柱特殊要求GB/T5779.3-2000. 中国标准出版社, 北京.

[8] 中华人民共和国国家标准 (1995) 滚丝轮GB/T971-94. 中国标准出版社出版, 北京.

分享
Top