硅钙合金球在430不锈钢冶炼中的应用
The Applications of the Calcium Silicon Alloy in 430 Stainless Steel during Smelting Process

作者: 陈兴润 :酒钢集团宏兴股份不锈钢分公司,嘉峪关;

关键词: 430不锈钢硅钙合金球夹杂物430 Stainless Steel Calcium Silicon Alloy Inclusions

摘要:

在AOD出钢过程中随钢流加入硅钙合金球,研究硅钙合金球对430不锈钢钢水质量的影响。结果表明:硅钙合金球对改善AOD炉渣流动性有一定作用;使用硅钙合金球的炉次跟未使用的炉次相比,AOD出钢前后全氧的降低量大6 ppm,AOD出钢后炉渣中的Cr2O3含量低0.07%;使用硅钙合金球的炉次,钢水中夹杂物类型为CaO-SiO2-Al2O3,中包中夹杂物尺寸以0~10 μm为主。

Abstract: Calcium silicon alloy was added into the liquid steel with steel flow after AOD refining, and the ef- fect of the calcium silicon alloy on the steel quality was studied. The results show that adding cal- cium silicon alloy has a role of improving slag fluidity. The decreased value of total oxygen before and after AOD tapping is 6 ppm more than that of unused calcium silicon alloy, and the Cr2O3 con- tent of slag after the steel tapping is down 0.07%. The inclusion type in the steel using calcium sil- icon alloy is mainly CaO-SiO2-A12O3, and the inclusion size in the tundish is mostly 0 - 10 μm.

文章引用: 陈兴润 (2014) 硅钙合金球在430不锈钢冶炼中的应用。 冶金工程, 1, 6-10. doi: 10.12677/meng.2014.11002

参考文献

[1] 黄宗泽, 池和冰, 李双江, 等 (2011) SUS430不锈钢夹杂物的变化规律研究. 宝钢技术, 1, 6-10.

[2] 李阳, 李伟坚, 姜周华, 等 (2009) 复合脱氧剂对430不锈钢脱氧行为的影响. 北京科技大学学报, 12, 100-103.

[3] Mapelli, C. and Nolli, P. (2003) Formation mechanism of non-metallic inclusions in different stainless steel grades. ISIJ International, 43, 1191-1199.

[4] 付邦豪, 陈超, 成国光, 等 (2012) 430不锈钢冶炼过程的夹杂物. 钢铁, 1, 40-43.

[5] Young Jo, K., Fan, L., Kazuki, M., et al. (2006) Mechanism study on the formation of liquid calcium aluminate inclu- sion from MgO-Al2O3 spinel. Steel Research International, 77, 785-792.

分享
Top