宽带发光铒铋共掺石英预制棒的制备
Fabrication of Er/Bi Co-Doped Silica Preforms with a Broadband Infrared Emission

作者: 吴金东 :深圳市光纤传感工程研究开发技术中心,深圳;深圳太辰光通信股份有限公司,深圳; 吴兴坤 :浙江大学现代光学仪器国家重点实验室,杭州;

关键词: MCVD溶液掺杂铒铋共发光宽带发光Modified Chemical Vapor Deposition Solute Doping Common Luminous Phenomenon of Erbium and Bismuth Near-Infrared Broadband Luminescence

摘要: 采用MCVD结合溶液掺杂技术制备了铒铋共掺的SiO2-Al2O3-GeO2光纤预制棒,测试其吸收和发射光谱,观测到铒铋宽带共同发光现象,该结果对于开发新型宽带放大光纤材料有指导意义,所得到的预制棒可望用于1.3 um窗口和S波段新型光纤放大器的研究。

Abstract: The modified chemical vapor deposition (MCVD) combing solution doping method is applied to the fabrication of erbium and bismuth-doped Silica preforms. Erbium and bismuth co-doped SiO2-Al2O3-GeO2 preforms with near-infrared broadband luminous are realized. The characteristic spectra of preforms are experimentally investigated, and the common luminous phenomenon of erbium and bismuth is observed. The experimental results are of instructive significance for developing new optical fiber materials of wideband amplification and the prepared erbium and bismuth-doped optical fiber preforms are expected to be used for the study on the new amplifier with 1.3 um window and S wave band.

文章引用: 吴金东 , 吴兴坤 (2014) 宽带发光铒铋共掺石英预制棒的制备。 光电子, 4, 6-12. doi: 10.12677/OE.2014.41002

参考文献

[1] Mori, A., Sakamoto, T., Kokayashi, K., et al. (2001) 1.58 µm broad-band Erbium-doped tellurite fiber amplifier. Journal of Lightwave Technology, 20, 822-827.

[2] 周亚训, 王大刚, 杨高波, 陈芬 (2010) 掺Er3+碲硼酸盐玻璃1.53 μm波段荧光强度提高研究. 光电子.激光, 7, 1031-1035.

[3] 吴昭君, 孙江亭, 张家骅, 骆永石, 吕树臣, 等 (2008) 新型掺铒碲酸盐玻璃光谱性质和热稳定性研究. 光电子.激光, 8, 1067-1071.

[4] 周大成, 王荣飞, 宋志国, 尹兆益, 杨正文, 邱建备 (2010) Er3+-Tm3+共掺碲酸盐玻璃中近红外超宽带发光性质. 硅酸盐学报, 11, 2115-2128.

[5] Qian, Q., Wang, Y., Zhang, Q.Y., et al. (2008) Spectroscopic properties of Er3+-Doped Na2O-Sb2O3-B2O3-SiO2 glasses. Journal of Non-Crystalline Solids, 354, 1981-1984.

[6] 王琰, 钱奇, 杨钢锋, 张勤远, 姜中宏 (2007) 掺铒锑硅酸盐玻璃光谱性质的研究. In: 中国硅酸盐学会特种玻璃分会第三届全国特种玻璃会议论文集.

[7] Seneschal, K., Jiang, S., Luo, T., et al. (2001) Er3+-doped alkaline free phosphate glasses for optical fiber amplifiers. Proceedings of SPIE, 4282, 93-100.

[8] Tanaka, S., Imai, K., Yazaki, T. and Tanaka, H. (2002) Ul-tra-wideband L-band EDFA using phosphorus co-doped silica-fiber. Proceedings of OFC’02, 458-459.

[9] 盖娜, 周亚训, 戴世勋, 徐铁峰, 聂秋华 (2008) 掺铒铋基玻璃的荧光俘获和浓度猝灭效应研究. 光电工程, 10, 58-62.

[10] 贾相华, 吕树臣 (2007) Er3+及Er3+/Yb3+共掺铋酸盐玻璃光谱性质研究. 物理学报, 8, 4971-4976.

[11] Wu, J.D., Chen, D.P., Wu, X.K. and Qiu, J.R. (2011) Ultra-broad near-infrared emission of Bi-doped SiO2-Al2O3GeO2 optical fibers. Chinese Optics Letters, 9, 071601.

[12] 吴金东, 陈丹平, 卢卫民, 张立永, 吴兴坤, 邱建荣 (2011) 近红外宽带发光掺铋石英光纤的研制. 光学学报, 4, 0406003.

[13] 赵鹤玲, 夏海平 (2012) Bi离子掺杂GeO2-Nb2O5-X玻璃的近红外宽带发光特性研究. 光电子.激光, 1, 106-110.

[14] Bufetov, I.A., Firstov, S.V., Khopin, V.F., et al. (2008) Bi-doped fiber lasers and amplifiers for a spectral region of 1300 1470 nm. Optics Letters, 33, 2227-2229.

[15] Peng, M., Zollfrank, C. and Wondraczek, L. (2009) Origin of broad NIR photoluminescence in bismuthate glass and Bi-doped glasses at room temperature. Journal of Physics: Condensed Matter, 21, 285106.

[16] Qiu, J., Peng, M., Ren, J., et al. (2008) Novel Bi-doped glasses for broadband optical amplification. Journal of NonCrystalline Solids, 354, 1235.

分享
Top