混凝法预处理冷轧钢废乳化液的研究
Study on Pretreatment of Waste Emulsion from Cold Rolling by Coagulation

作者: 张 薇 , 王 楠 :辽宁科技大学,鞍山; 单明军 :北京万邦达环保技术股份有限公司,北京;

关键词: 混凝法废乳化液聚合氯化铝铁聚丙烯酰胺Coagulation Waste Emulsion PAFC PAM

摘要:

 本实验采用混凝法对某钢厂冷轧钢废乳化液进行预处理,该废乳化液的浊度为3900NTU,COD为16,400mg/L。实验结果表明,聚合氯化铝铁具有一般铝盐和铁盐破乳剂的双重优点,将它与非离子型聚丙烯酰胺联合使用对冷轧钢废乳化液进行预处理时取得了良好的效果。在pH值为7.3,聚合氯化铝铁用量为1600mg/L,非离子型聚丙烯酰胺用量为1.5 mg/L的情况下处理废乳化液,出水剩余浊度为75 NTU,COD去除率可达97.2%。

Abstract:   In this study, the process of coagulation is adopted to pretreat the waste emulsion from cold rolling. The turbidity of waste emulsion is 3900 mg/L. The COD (Chemical Oxygen Demand) is 16,400 mg/L. The results show that PAFC has the dual advantages of general aluminum and iron salts. It is one of the most suitable demulsifiers. It has achieved such a good result when making the PAFC and the non-ionic PAC used in combination to pretreat the waste emulsion from cold rolling. To treat the waste emulsion from cold rolling, the optimum conditions are pH 7.3, 1600 mg/LPAFC and 1.5 mg/L non-ionic PAC.

文章引用: 张 薇 , 单明军 , 王 楠 (2014) 混凝法预处理冷轧钢废乳化液的研究。 水污染及处理, 2, 1-4. doi: 10.12677/WPT.2014.21001

参考文献

[1] 高红, 张天胜 (2005) 含油废水处理技术进展. 天津化工, 1, 28-31.

[2] 倪伟敏, 陈春明, 徐根良 (2003) 混凝法处理废乳化液的研究. 环境污染与防治, 1, 39-42.

[3] Li, Z.Y., Song, C.Y. and Wang, L. (2008) Technique and application of treating cold rolling emulsion wastewater. Journal of Environmental Engineering, 26, 48.

[4] 黄敏 (2007) 包钢冷轧含油废水处理工艺分析及生物降解特性分析. 西安建筑科技大学, 西安.

[5] 刘万, 胡伟 (2006) 浅谈超滤法处理钢铁企业冷轧厂乳化液废水. 工业水处理, 7, 24-28.

[6] 梁民勤, 彭仕军 (2009) 冷轧废水处理及新技术应用. 柳钢科技, 1, 30-33.

[7] 张耀斌, 王鸿道 (1996) 混凝–生物接触氧化–煤渣灰吸附工艺治理废乳化液的研究. 环境保护, 1, 16-17.

[8] 咚瑞利, 赵娜娜, 刘成蹊等 (2007) 有机高分子絮凝剂絮凝机理及进展. 河北化工, 3, 3-6.

分享
Top