硅铝比对无碱铝硼硅酸盐玻璃高温粘度 和析晶性能的影响
Effect of the Ratio of SiO2 and Al2O3 on the Viscosity and Crystallization of Non-Alkali Aluminoborosilicate Glasses at High Temperature

作者: 田中青 * , 朱昱恺 , 黄伟九 , 李喜林 :重庆理工大学材料科学与工程学院,重庆; 杜 迅 :重庆国际复合材料有限公司,重庆;

关键词: 粘度成型温度析晶Viscosity Fiber-Drawing Temperature Crystallization Template

摘要: 研究了硅铝比对无碱铝硼硅酸盐玻璃高温粘度和析晶性能的影响。结果表明,随着硅铝比的增加,无碱铝硼硅酸盐系统玻璃的高温粘度、成型温度和粘滞活化能增加,液相温度降低,成型温度与液相线温度的差值增大。

Abstract: Effect of the ratio of SiO2 and Al2O3 on the viscosity and crystallization of non-alkali aluminoborosilicate glasses at high temperature was investigated. The results showed that the viscosity, the fiber-drawing temperature and the activation energy for vicious flow were increased, the liquidus temperature was decreased and the difference between the fiber-drawing temperature & the liquidus temperature was increased with the ratio of SiO2 and Al2O3 increased.

文章引用: 田中青 , 朱昱恺 , 黄伟九 , 杜 迅 , 李喜林 (2013) 硅铝比对无碱铝硼硅酸盐玻璃高温粘度 和析晶性能的影响。 化学工程与技术, 3, 82-85. doi: 10.12677/HJCET.2013.33015

参考文献

[1] 王中俭, 陈兴芬, 胡一晨等. 电子玻璃纤维介电性能和工艺参数的研究[J]. 材料科学与工艺, 2007, 15(5): 662-664, 669.

[2] 徐言超, 岳云龙, 于晓杰, 陈现景等. 正交实验研究硼铝硅玻璃的介电性能[J]. 绝缘材料, 2007, 40(3): 48-51.

[3] 沈龙. 印制电路板的新玻璃成分[J]. 玻璃纤维, 2002, 3: 14- 15.

[4] 杨盟辉. 高频PCB基材介电常数与介电损耗的特性与改性进展[J]. 印制电路信息, 2009, 4: 27-31.

[5] 欧辉生. 国内外电子级玻璃纤维生产现状及市场发展趋势[J]. 印制电路板信息, 2005, 9: 23-25.

[6] P. Choudhury, S. K. Pal and H. S. Ray. On the prediction of vis- cosity of glasses from optical basicity. Journal of Applied Phys- ics, 2006, 100(1): 1-5.

[7] 段仁官, 梁开明, 顾守仁等. CaO-Al2O3-SiO2系统剥离晶化时析晶相及TiO2的作用机理预测和研究[J]. 硅酸盐雪豹, 1997, 25(3): 305-311.

分享
Top